Interrelation of Microstructure and Corrosion Resistance in Biodegradable Magnesium Alloys with Aluminum, Lithium and Rare Earth Additions

Publication at Faculty of Mathematics and Physics |
2015

Abstract

The influence of equal channel angular pressing and rotary swaging on the microstructure and corrosion resistance was investigated in three magnesium alloys with the addition of aluminum, lithium and rare earth elements - AE21, AE42 and LAE442. The processing resulted in grain refinement in all cases; nevertheless, the effect on the corrosion resistance was ambiguous.

A continuous increase of the polarization resistance during the gradual equal channel angular pressing was observed in the AE42 and LAE442 alloys, whereas there was almost no effect in the AE21 alloy. The rotary swaging of AE42 resulted in a decrease of polarization resistance.

The increase of polarization resistance in the alloys with the higher concentration of alloying elements was caused by the combined effect of grain refinement and better dispersion of particles in the matrix thanks to shear deformation during equal channel angular pressing. In the AE42 alloy, the increase of the corrosion resistance after equal channel angular pressing was also proven by chemical analysis of the solution and acoustic emission detection.

This beneficial effect was not observed when the concentration of alloying elements was lower or when the deformation mode was different from shearing.