Thermal Stability of Microstructure of High-Entropy Alloys Based on Refractory Metals Hf, Nb, Ta, Ti, V, and Zr
Abstrakt
In the present work, a series of high-entropy alloys based on refractory metals Hf, Nb, Ta, Ti, V, and Zr with various compositions have been systematically investigated. Our study revealed that a bcc single-phase solid solution of a Hf-Nb-Ta-Ti-V-Zr system is thermodynamically stable only at high temperatures above 1000 degrees C.
At lower temperatures, the phase separation into disordered bcc phases with slightly different chemical compositions occurs. Despite the phase separation, a single-phase random solid solution can be saved at room temperature as a metastable phase by rapid cooling of the sample from high temperature.
The microstructure of a single-phase metastable random solid solution was characterized and compared with the microstructure of the as-cast state. Furthermore, the mechanical properties of annealed and as-cast alloys were compared.
Interestingly, both states exhibit comparable mechanical properties. It indicates that from the point of view of practical applications, a mechanical mixture of disordered bcc solutions is as good as single-phase random solid solution.