Abstrakt
Hexagonal rare-earth manganese oxide YMnO(3) thin films were prepared on yttria-stabilized zirconia (111) substrates by metal organic decomposition method. The crystallinity and morphology of YMnO(3) thin films crystallized at various temperatures were examined by X-ray diffraction and atomic force microscopy measurements, respectively.
Single phase YMnO(3) was obtained for the sample prepared by annealing temperatures of 950 °C. AFM analysis revealed that a smooth surface with a roughness of 0.15 nm was achieved for YMnO(3) thin film annealed at 950 °C and 1000 °C, while three-dimensional growth for other samples prepared at 750-900 °C, 1050 °C, and 1100 °C.
A narrow band at 1.6 eV and a broad band at 5 eV due to electronic transitions in the manganese and oxygen bands were observed in an absorption spectrum.