Abstract
The effect of ECAP technology (the number of passes N = 2, 4, 8, 12) and subsequent annealing on the subgrain structure of coarse-grained pure aluminium is described by means of the orientation imaging microscopy. The local and overall non-homogeneity and anisotropy of boundary structures have also been evaluated.